"HIGLOSS" Semi-shrinkable BOPP Film

"HIGLOSS" Semi-shrinkable BOPP Film Distinguished gloss. High transparency. Excellent abrasion resistance. Good heat shrinka

Types:

RCO-83: Small Pack

RCO-83A: Bar Pack

Specification:

Type	Thickness (μm)	Width (mm)	Roll Diameter (mm)
RCO-83   RCO-83A	18 ~25μm	117~1200	200~500

Characteristics:

       Distinguished gloss.

       High transparency.

       Excellent abrasion resistance.

       Good heat shrinkage, specially ideal for tight package contributed to the unique properties of inside surface.

       Low static.

       Perfect surface slip (even in the condition of 600C).

       High stiffness, good foldability.

       Good heat sealability in high speed.

Typical Physical Properties

Items		Methods	Units	RCO-83	RCO-83A
Thickness		GB/T 6672-1986	μm	21.2	21.1
Tensile Strength (MD/TD)		GB/T 13022-1991	MPa	172/296	159/301
Elongation at Break (MD/TD)		GB/T 13022-1991	%	158/53	158/56
Modulus    (MD/TD)		GB/T 13022-1991	MPa	2620/4830	2530/4810
Heat Shrinkag(MD/TD)		120°C×1 min	%	5.8/5.6	5.1/4.8
Haze		GB/T 2410-1988	%	1.0	1.2
Gloss		GB/T 8807-1988	%	96.4	95.0
C.O.F	in - in	GB/T 10006-1988	Static/Dynamic	0.42/0.30	0.45/0.31
	out-out			0.33/0.20	0.35/0.20
Seal Strength	in - in	135°C×1s×0.18MPa	N/15mm	3.1	3.0
	in– out			3.2	3.1
	out-out			3.1	3.2

Notes:

MD: Machine Direction; TD: Transverse Direction.

The above data can only be regarded as typical physical properties, not guarantee values.

Application:

The products are applied in hard-box package ,such as cigarette package ,medicine package.

Industrial Standards

“Biaxially oriented polypropylene shrink film for heat-seal ”.

National Standardof the People’s Republic of China.

(Standard Code: GB/T 12026-2000)

Transportation and Storage Notices:

Any impact or collision during transporting, loading and unloading may result in the damage of roll surface and edge. Storage in shady, cool and dry condition avoiding direct sunshine and rain is recommended. 

"HIGLOSS" Semi-shrinkable BOPP Film